| Item | Unit | Data | ||||
| RBSiC(SiSiC) | NBSiC | SSiC | RSiC | OSiC | ||
| SiC content | % | 85 | 75 | 99 | ≥99 | ≥90 |
| Free silicon content | % | 15 | 0 | 0 | 0 | 0 |
| Max service temperature | ℃ | 1380 | 1450 | 1650 | 1620 | 1400 |
| Density | g/cm3 | 3.02 | 2.75-2.85 | 3.08-3.16 | 2.65-2.75 | 2.75-2.85 |
| Open porosity | % | 0 | 13-15 | 0 | 15-18 | 7-8 |
| Bending strength 20℃ | Mpa | 250 | 160 | 380 | 100 | / |
| Bending strength 1200℃ | Mpa | 280 | 180 | 400 | 120 | / |
| Modulus of elasticity 20℃ | Gpa | 330 | 580 | 420 | 240 | / |
| Modulus of elasticity 1200℃ | Gpa | 300 | / | / | 200 | / |
| Thermal conductivity 1200℃ | W/m.k | 45 | 19.6 | 100-120 | 36.6 | / |
| Coefficient of thermal expansion | K-1×10-6 | 4.5 | 4.7 | 4.1 | 4.69 | / |
| HV | kg/mm2 | 2115 | / | 2800 | / | / |
| Maximunm operating temperature (℃) | Density(g/cm3) | Heat conduction [W/(m℃)] | Specific heat capacity[KJ/(kg℃)] |
| 1500 | 2.2-2.4 | 23.26 | 0.71 |
| Resistivity (Ω-mm2/m) | Thermal expansion coefficient (20-1500℃)(×10-6/℃) | Tensile strength (MPa) | Flexural strength(MPa) |
| 1000-2000 | 5 | 39.2-49 | 70-90 |
| Diameter | Heating zone length | Cold zone length | Overall length | Range of resisitance |
| 14mm | 100-500mm | 150-350mm | 400-1200mm | 0.7-5.6 ohms |
| 16mm | 200-600mm | 150-350mm | 500-1600mm | 0.7-4.4 ohms |
| 18mm | 200-800mm | 150-400mm | 500-1600mm | 0.7-5.8 ohms |
| 20mm | 200-800mm | 200-600mm | 600-2000mm | 0.6-6.0 ohms |
| 25mm | 200-1200mm | 250-700mm | 700-2600mm | 0.4-5.0 ohms |
| 30mm | 300-2000mm | 250-800mm | 800-3600mm | 0.4-4.0 ohms |
| 35mm | 400-2000mm | 250-800mm | 900-3600mm | 0.5-3.6 ohms |
| 40mm | 500-2700mm | 250-800mm | 1000-4300mm | 0.5-3.4 ohms |
| 45mm | 500-3000mm | 250-750mm | 1000-4500mm | 0.3-3.0 ohms |
| 50mm | 600-2500mm | 300-750mm | 1200-4000mm | 0.3-2.5 ohms |
| 54mm | 600-2500mm | 300-750mm | 1200-4000mm | 0.3-3.0 ohms |
| Maximum temperature and the surface load of silicon carbide element in a different atmosphere | ||
| Atmosphere | Using temperature (℃) | Elements surface load (W/cm2) |
| Ammonia/Hydrogen | 1300 | 4.6 |
| Air | 1500 | 4.0 |
| Nitrogen | 1400 | 4.6 |
| Carbon dioxide | 1500 | 3.8 |
| Carbon monoxide | 1530 | 3.8 |
| Water vapor | 1200 | 4.6 |
| Hydrocarbons | 1320 | 3.1 |
| Sulfur/sulfur dioxide | 1320 | 3.8 |
| Vacuum | 1200 | 3.8 |
| Halogen | 700 | 3.8 |
Silicon carbide heating rods are widely applied to high-temperature electric furnaces and heating equipment. They serve industries like magnetic materials, powder metallurgy, ceramics, glass, metallurgy and machinery.
The two packing methods we use are plywood box packing and solid wood packing, with the solid wood box requires a fumigation certificate. Depending on the various products, we will tailor the proper packaging box; Plastic foam measuring 2 cm to 3 cm thick is placed within the box and secured with row nails. To maintain the products safety during shipment, packing tape is typically used.
We can clearly know how to ensure the output of products and quality stability and manufacture silicon carbide ceramic products with superior performance.
Newthink New Material Co., Ltd. is located in Qingdao West Coast New Area, China. Established in 2011, it is a professional manufacturer engaged in the research, development, production and sales of silicon carbide ceramic products, with two subsidiaries; and sub-brands.
Qingdao Newthink New Materials Co., Ltd.
ADD: NO.448, Jiangshan South Road, Qingdao City,China
TEL: +86 532 86941661
FAX: +86 532 86941661
EMAIL: info@siliconcarbideo.com